| Quantity: | |
|---|---|
CHEMICAL COMPOSITION
C: 1.5-1.6
Si: 0.1-0.4
Mn: 0.15-0.45
P: ≤ 0.03
S: ≤ 0.03
Cr: 11.0-12.0
V: 0.9-1.1
Mo: 0.6-0.8
MECHANICAL PROPERTIES
Hardness: In factory condition, the hardness does not exceed 235HB. After heat treatment, the hardness can reach 60-65HRC.
Yield strength: can reach more than 1200MPa.
PHYSICAL PROPERTIES
Thermal conductivity: The thermal conductivity is 21 W/m K at 100°C.
Density: At 20°C, the density is 7700 g/cm³, and the density decreases slightly as the temperature increases.
Elastic modulus: At 20°C, the elastic modulus is 210000 MPa. As the temperature increases, the elastic modulus decreases.
HEAT TREATMENT
Pre-heat Temperature: 840-860℃
Quenching Temperature: 1020-1050℃
Quenching Medium: oil,hot bath,air
Tempering Temperature: 150-200℃ Followed by Quenching
Hardness: Min 60HRC
Ac1: 830℃
Ac3: 855℃
Ar1: 750℃
Ms: 230℃
FORGING
Initial Forging Temperature：1010-1200℃
Final Forging Temperature：above 927℃
Forging Ratio：above 4:1
Cooling Method After Forged:As high carbon cold work tool steel ,DIN 1.2379 steel should be annealed after forging.
CHEMICAL COMPOSITION
C: 1.5-1.6
Si: 0.1-0.4
Mn: 0.15-0.45
P: ≤ 0.03
S: ≤ 0.03
Cr: 11.0-12.0
V: 0.9-1.1
Mo: 0.6-0.8
MECHANICAL PROPERTIES
Hardness: In factory condition, the hardness does not exceed 235HB. After heat treatment, the hardness can reach 60-65HRC.
Yield strength: can reach more than 1200MPa.
PHYSICAL PROPERTIES
Thermal conductivity: The thermal conductivity is 21 W/m K at 100°C.
Density: At 20°C, the density is 7700 g/cm³, and the density decreases slightly as the temperature increases.
Elastic modulus: At 20°C, the elastic modulus is 210000 MPa. As the temperature increases, the elastic modulus decreases.
HEAT TREATMENT
Pre-heat Temperature: 840-860℃
Quenching Temperature: 1020-1050℃
Quenching Medium: oil,hot bath,air
Tempering Temperature: 150-200℃ Followed by Quenching
Hardness: Min 60HRC
Ac1: 830℃
Ac3: 855℃
Ar1: 750℃
Ms: 230℃
FORGING
Initial Forging Temperature：1010-1200℃
Final Forging Temperature：above 927℃
Forging Ratio：above 4:1
Cooling Method After Forged:As high carbon cold work tool steel ,DIN 1.2379 steel should be annealed after forging.